Laser-induced crystallization in vanadate glasses

Relatore
Mario Affatigato - Coe College, Iowa, visiting professor at Physics Dep of Trento
Data e ora
giovedì 24 aprile 2008 alle ore 10.30
Luogo
Ca' Vignal - Piramide, Piano 0, Sala Verde
Referente
Gino Mariotto
Referente esterno
Data pubblicazione
18 aprile 2008
Dipartimento
 

Riassunto

We report on our investigation of the effects of 785 nm light irradiation on lead and barium vanadate glasses. Whereas high powers (>84 mW) yielded crystallization and thermal modification of the surface, low powers (<38 mW) altered the sample without causing crystal formation. Scanning probe microscopy, scanning electron microscopy, EDX, and micro-Raman spectroscopy were used to characterize the changes induced by the laser light. As part of the work we made glasses in the range 10 < x < 60, where x is the molar percent of lead and/or barium oxide, as well as crystals corresponding to 2PbO.V2O5, 3PbO.V2O5, and 8PbO.V2O5. We also looked at the crystallization of other binary vanadate glass families. The healing of low-power damaged areas by annealing was studied, and we also made calorimetric measurements on the glasses. In general, the results point to a laser-assisted diffusion of lead and/or barium, which helps establish the right stoichiometric conditions for crystallization upon cooling from the laser irradiation. This research was supported by the National Science Foundation under grant DMR-CER-0502051, and by the Roy J. Carver Charitable Trust of Iowa.






© 2002 - 2021  Universit√† degli studi di Verona
Via dell'Artigliere 8, 37129 Verona  |  P. I.V.A. 01541040232  |  C. FISCALE 93009870234